http://repositoriodigital.ipn.mx/handle/123456789/11246| Título : | Spray-pyrolyzed hydroxyapatite thin-film coatings |
| Palabras clave : | Spray Pyrolysis Hydroxyapatite XPS XRD |
| Fecha de publicación : | 16-ene-2013 |
| Editorial : | ELSEVIER |
| Descripción : | Hydroxyapatite (HA) thin-film coatings have been deposited on sheet substrates of a commonly used
biomaterial (Ti6Al4V) using the spray pyrolysis technique. For this, a 0.042 M calcium spraying solution was
prepared by dissolving calcium acetylacetonate hydrate in N,N-dimethylformamide, and phosphoric acid
(H3PO4) was used as the source of phosphorous with different volume concentrations in deionized water.
Both the solutions were supplied simultaneously and in parallel during the deposition of the coatings. The
coatings were deposited at substrate temperatures of 425 and 525 °C. The use of 0.27% (volume) solution of
H3PO4 resulted in coatings with stoichiometry close to that of the HA. The chemical composition, surface
morphology and structure of the HA coatings were investigated by X-ray photoelectron spectroscopy (XPS),
scanning electron microscopy (SEM) and X-ray diffraction (XRD). The characteristics of the coatings thus
observed are presented and discussed. The high purity of the coatings was revealed by XPS, confirming the
presence of Ca, P and O as the main constituents, with a Ca/P ratio of about 1.3. Some carbon, inherent to the
precursors used, was also detected by XPS. The XRD patterns obtained suggested preferred (113) and (321)
crystal orientations in the coatings. Investigación INSTITUTO POLITECNICO NACIONAL |
| URI : | http://www.repositoriodigital.ipn.mx/handle/123456789/11246 |
| Otros identificadores : | Surface & Coatings Technology 204 (2009) 1116-1120 0257-8972 http://hdl.handle.net/123456789/761 |
| Aparece en las colecciones: | Doctorado |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 2009-1 1.pdf | 657.76 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.