El Instituto Politécnico Nacional
Contribuye al desarrollo económico y social de la nación, a través de la formación integral de personas competentes; de la investigación, el desarrollo tecnológico y la innovación. Además tiene reconocimiento internacional por su calidad e impacto social.
Por favor, use este identificador para citar o enlazar este ítem:
http://repositoriodigital.ipn.mx/handle/123456789/10676Registro completo de metadatos
| Campo DC | Valor | Lengua/Idioma |
|---|---|---|
| dc.creator | Valverde Aguilar, Guadalupe | - |
| dc.creator | García Macedo, Jorge | - |
| dc.creator | Galvan Ramirez, Pablo | - |
| dc.creator | Renteria Tapia, Victor | - |
| dc.date | 2012-03-16T16:24:50Z | - |
| dc.date | 2012-03-16T16:24:50Z | - |
| dc.date | 2009 | - |
| dc.date.accessioned | 2013-01-16T09:00:10Z | - |
| dc.date.available | 2013-01-16T09:00:10Z | - |
| dc.date.issued | 2013-01-16 | - |
| dc.identifier | 0277-786X | - |
| dc.identifier | http://hdl.handle.net/123456789/158 | - |
| dc.identifier.uri | http://www.repositoriodigital.ipn.mx/handle/123456789/10676 | - |
| dc.description | Nanocrystalline TiO2 films doped with gold nanoparticles were synthesized by the sol–gel process at room temperature. The TiO2 films were synthesized by using tetrabutyl orthotitanate as the inorganic precursor. The films were spin-coated on glass wafers. The samples were annealed at 100°C for 30 minutes and sintered at 520°C for 1 hour to generated anatase and rutile phases. The films were characterized using UV-Vis absorption spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy. An absorption peak located at around 651 nm is due to the surface plasmon resonance of the gold nanoparticles. Optical absorption spectrum was fitted by Gans model by using a high refractive index (nlocal = 2.6). This high index is related to the high content of anatase nanoparticles embedded in the film. Photoconductivity studies were performed on nanocrystalline (anatase phase) films. The experimental data were fitted with straight lines at darkness and under illumination at 515 nm and 645 nm. This indicates an ohmic behavior. Transport parameters were calculated. Results are discussed. | - |
| dc.language | en | - |
| dc.publisher | SPIE Proceedings | - |
| dc.subject | Gold nanoparticles | - |
| dc.subject | Titania | - |
| dc.title | Synthesis, characterization, and photoconductivity studies on amorphous and nanocrystalline TiO2 films doped with gold nanoparticles | - |
| dc.type | Article | - |
| Aparece en las colecciones: | Doctorado | |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 7393_33 Synthesis TiO2_Au NPs 2009.pdf | 397.63 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.